地聚合物对水泥固化土强度的影响及其机理分析

邓永锋; 吴子龙; 刘松玉; 岳喜兵; 朱雷雷; 陈江华; 关云飞

doi:10.11779/CJGE201603007

地聚合物对水泥固化土强度的影响及其机理分析 English Version

1. 东南大学交通学院岩土工程研究所,江苏南京 210096;
2. 江苏省公路局,江苏南京210004;
3. 江苏省交通工程集团有限公司,江苏镇江212016;
4. 南京水利科学研究院岩土工程研究所, 江苏南京 210024

基金项目: 国家自然科学基金项目(41572280,51378117,41330641,51208321); 江苏省交通运输科技与成果转化计划项目(2010Y36-1)

详细信息

作者简介:
邓永锋(1978- ),教授,博士生导师,主要从事地基处理与软黏土基本工程特性研究.E-mail: noden@seu.edu.cn.

中图分类号: TU433
计量
- 文章访问数: 568
- HTML全文浏览量: 13
- PDF下载量: 564
出版历程
- 收稿日期: 2014-11-15
- 发布日期: 2016-03-24

Influence of geopolymer on strength of cement-stabilized soils and its mechanism

1. Institute of Geotechnical Engineering, Transportation College, Southeast University, Nanjing 210096, China;
2. Highway Department of Jiangsu Province, Nanjing 210004, China;
3. Traffic Engineering Group Co., Ltd., of Jiangsu Province, Zhenjiang 212016, China;
4. Geotechnical Engineering Department, Nanjing Hydraulic Research Institute, Nanjing 210024, China

摘要

摘要: 采用无侧限抗压强度,电镜扫描(SEM)和压汞(MIP)等试验方法,分析研究了地聚合物--偏高岭土(metakaolin)对水泥土的力学强度的影响规律,探讨了其改善水泥土强度的机理,并根据现场测试验证了实用性和经济性.试验结果表明:地聚合物掺入水泥土后,水泥土的无侧限抗压强度得到了大幅度的提高,然而强度与地聚合物掺量之间并非单一线性增加关系,而是由活性区域和惰性区域组成,转折点对应的MK掺量为3%;微观试验结果表明地聚合物掺入能产生更多的胶结物,使水泥土结构更加致密;基于试验数据给出了地聚合物掺量与水泥土强度增长的评价公式.现场测试结果和工程造价分析均表明了地聚合物具有较大的工程实用性.
- 水泥土 /
- 地聚合物 /
- 偏高岭土 /
- 无侧限抗压强度 /
- 机理分析 /
- 现场测试
Abstract: The unconfined compression shearing tests, scanning electron microscopy (SEM) and mercury intrusion porosimetry (MIP) methods are used to clarify the strength behavior and microstructural evolution of cement-stabilized soils with geopolymer (metakaolin), and then the in-situ tests are conducted to verify their practicability and economy. The results show that when the geopolymer MK is incorporated into the cement, the strength of cement-stabilized soils is obviously multiplied, and significantly better than that modified just by the pure cement, which means that the strength behavior of cemented soils can be further improved. It should be noted that the strength of cement-stabilized soils does not linearly increase with the mixing ratio of geopolymer; its growth efficiency can be divided into the active and inert zones; and the threshold mixing ratio of MK is 3% in this case. The microstructural analysis shows that the MK incorporation can produce more cementation and make the sample denser. Furthermore, the proposed strength enhancement prediction model also verifies these findings. Finally, the analysis of the in-situ strength and economy also shows its effectiveness and the potential engineering application.
- cement-stabilized soil /
- geopolymer /
- metakaolin /
- unconfined compression shearing test /
- micromechanism /
- in-situ test

HTML全文

参考文献(27)

[1]	POON C S, KOU S C, LAM L. Compressive strength, chloride diffusivity and pore structure of high performance metakaolin and silica fume concrete[J]. Construction and Building Materials, 2006, 20: 858-865.
[2]	WILD S, KHATIB J M, JONES A. Relative strength, pozzolanic activity and cement hydration in superplasticised metakaolin[J]. Cement and Concrete Research, 1996 26(10): 1537-1544.
[3]	AMBROISE J, MAXIMILIEN S, PERA J. Properties of metakaolin blended cements[J]. Advanced Cement Research,1994, 1(4): 161-168.
[4]	LI Z J, DING Z. Property improvement of Portland cement by incorporating with metakaolin and slag[J]. Cement and Concrete Research, 2003, 33(4): 579-584.
[5]	LAGIER F, KURTIS K E. Influence of Portland cement composition on early age reactions with metakaolin[J]. Cement and Concrete Research, 2007, 37: 1411-1417.
[6]	GESOGLU E G, MERMERDAS K. Improving strength, drying shrinkage, and pore structure of concrete using metakaolin[J]. Materials and Structures, 2008, 41: 937-949.
[7]	SHEKARCHI M, BONAKDAR A, BAKHSHI M, et al. Transport properties in metakaolin blended concrete[J]. Construction and Building Materials, 2010, 24(11): 2217-2223.
[8]	KHATIB J M, WILD S. Pore size distribution of metakaolin paste[J]. Cement and Concrete Research, 1996, 26(10): 1545-1553.
[9]	POON C S, LAM L, KOU S C, et al. Rate of pozzolanic reaction of metakaolin in high-performance cement pastes[J]. Cement and Concrete Research, 2001, 31: 1301-1306.
[10]	FRIAS M, RAJOS M I, CABRERA J. The effect that the pozzolanic reaction of metakaolin has on the heat evolution in metakaolin-cement mortars[J]. Cement and Concrete Research, 2000, 30: 209-216.
[11]	JUSTICE J M, KURTIS K E. Influence of metakaolin surface area on properties of cement-based materials[J]. Journal of Materials in Civil Engineering, 2007, 19: 762-771.
[12]	GRUBER K A, RAMLOCHAN T, BODDY A, et al. Increasing concrete durability with high-reactivity metakaolin[J]. Cement ＆ Concrete Composites, 2001, 23: 479-484.
[13]	BATIS G, PANTAZOPOULOU P, TSIVILIS S, et al. The effect of metakaolin on the corrosion behavior of cement mortars[J]. Cement ＆ Concrete Composites, 2005, 27: 125-130.
[14]	KIM H S, LEE S H, MOON H Y. Strength properties and durability aspects of high strength concrete using Korean metakaolin[J]. Construction and Building Materials, 2007, 21: 1229-1237.
[15]	POLOMO A, BLANCO M T, GRANIZO M L, et al. Chemical stability of cementitious materials based on metakaolin[J]. Cement and Concrete Research, 1999, 29: 997-1004.
[16]	ALAKHRAS N M Durability of metakaolin concrete to sulfate attack[J]. Cement and Concrete Research, 2006, 36: 1727-1734.
[17]	刘松玉, 钱国超, 章定文. 粉喷桩复合地基理论与工程应用[M]. 北京. 中国建筑工业出版社, 2006. (LIU Song-yu, QIAN Guo-chao, ZHANG Ding-wen. The principle and application of dry jet mixing composite foundation[M]. Beijing: China Architecture & Building Press, 2006. (in Chinese))
[18]	储诚富, 李小春, 邓永锋, 等. 偏高岭土对水泥改性海相黏土力学性能的影响[J]. 岩土工程学报, 2013, 35(增刊1): 170-174. (CHU Cheng-fu, LI Xiao-chun, DENG Yong-feng, et al. Influence of metakaolin on mechanical properties of cement-modified marine soft soil[J]. Chinese Journal of Geotechnical Engineering, 2013, 35(S1): 170-174. (in Chinese))
[19]	UDDIN K. Strength and deformation behavior of cement treated Bangkok clay[D]. Bangkok: Asian Institute of Technology, 1994.
[20]	BERGADO D T, ANDERSON L R, MIURA N, et al. Soft ground improvement in lowland and other environments[M]. Virginia: American Society of Civil Engineers Press, 1996.
[21]	HOPRIBULSUK S, RACHAN R, RAKSACHON Y. Role of fly ash on strength and microstructure development in blended cement stabilized silty clay[J]. Soils and Foundations, 2009, 49(1): 85-98.
[22]	LORENZO G A, BERGADO D T. Fundamental characteristics of cement-admixed clay in deep mixing[J]. Journal of Materials in Civil Engineering , 2006, 18(2): 161-174.
[23]	LORENZO G A, BERGADO D T. Fundamental parameters of cement-admixed clay-new approach[J]. Journal of Geotechnical and Geoenvironmental Engineering, 2004, 130(10): 1042-1050.
[24]	ZHANG D W, CAO Z G, FAN L B, et al. Effect of chloride salt concentration on unconfined compression strength of cement-treated Lianyungang soft marine clay[J]. Journal of Southeast University, 2013, 29(1): 79-83.
[25]	ZHANG D W, CHEN L, LIU S Y. Key parameters controlling electrical resistivity and strength of cement treated soils[J]. Journal of Central South University, 2012, 19: 2991-2998.
[26]	CONSOLI N C, FOPPA D, FESTUGATO L, et al. Key paramenters for strength control of artificially cemented soils[J]. Journal of Geotechnical and Geoenvironmental Engineering, 2007, 133(2): 197-205.
[27]	CONSOLI N C, CRUZ R C, FLOSS M F, et al. Parameters controlling tensile and compressive strength of artificially cemented sand[J]. Journal of Geotechnical and Geoenvironmental Engineering, 2010, 136(5): 759-763.

施引文献

资源附件(0)

计量

文章访问数: 568
HTML全文浏览量: 13
PDF下载量: 564
被引次数: 0

地聚合物对水泥固化土强度的影响及其机理分析 English Version

作者简介: 邓永锋(1978- ),教授,博士生导师,主要从事地基处理与软黏土基本工程特性研究.E-mail: noden@seu.edu.cn.

计量

出版历程

Influence of geopolymer on strength of cement-stabilized soils and its mechanism

计量

出版历程

目录

作者简介:
邓永锋(1978- ),教授,博士生导师,主要从事地基处理与软黏土基本工程特性研究.E-mail: noden@seu.edu.cn.